Tag: Rust and corrosion

How is corrosion prevented?

Bolt wrapping.Ton Hoa Phat
Bolt and nut corrosion protection in acid prone area
There are many ways to prevent corrosion, including modifying the atmosphere by dehumidification, nitrogen purge, evacuation, etc, and creating a barrier on the metal surface to prevent the permeation of moisture. This barrier can be formed by liquid coating, such as oil, or via a multiple-layer product set that works by: 1. From inside, the primer coat has good waterproofing performance, settles on metal surfaces and inhibits rust development by permeating rust layer because it is oil type; and 2. From outside, acting as a protective barrier against external corrosive atmospheric elements such as abrasion, oxygen, water, dirt, and acid gas pollutants. The Anti-UV membrane has good weatherbility, can shut out water and air that will lead to corrosion of metal surface. Click here for more details. Corrosion is now your terrible headache? Send us foto of your corrosion issues to kien@vinats.com or call us at +84981581661 for FREE site survey and all-round solution. Still doubt? see our case study HERE.

What is Corrosion | 4 typical types of corrosion

what is corrosion part 1

According to the Kennedy Space Center, corrosion can be defined as the deterioration of a material due to a chemical reaction with its environment over time. Metals corrode because they’re used in environments where they’re naturally unstable; and it’s a big problem for bridge, pipeline, plant builders and other architects who frequently use metal products in their structures.

There are various forms of corrosion. Below is a selection of just three forms of corrosion.

Uniform Corrosion

Let’s start with the basic form of corrosion first. You can think of uniform corrosion as rust, since it is the most common form of corrosion. And since rust is pretty common; it’s not a huge issue for architects to take care of. Using protective coatings like paint or a sealant can control uniform corrosion for short term but for long term control, a comprehensive solution is required. See how corrosion is prevented.

Galvanic Corrosion

Galvanic corrosion occurs when different metals come into contact with each other. This form of corrosion can easily be spotted where the two metals meet. Popular trinkets like insulating gaskets and washers can assist with staving off galvanic corrosion; but they will need to be replaced with regular maintenance.

 Concentration Cell Corrosion

Concentration cell corrosion occurs when two or more areas of a metal surface are in contact with each other; but corrode at different rates. There are three general types of concentration cell corrosion: Metal Ion Concentration Cells: This happens most commonly in water when a high concentration of metal ions are exposed crevices and become corroded over time. This can be prevented by sealing the exposed crevices to prevent water from coming into contact with the metal.
  • Oxygen Concentration Cells: This type of corrosion can occur in areas with low oxygen; like underneath wood, rubber, tape, and other materials. This can be minimized by sealing the exposed areas; keeping the surfaces clean, and avoiding materials that will create moisture between surfaces.
  • Active-Passive Cells: Some metals actually depend on thin films of corrosion product, called an active-passive cell, for corrosion protection. If this thin film is broken, the metal beneath the film will start to corrode. This type of corrosion can be avoided with regular cleaning and application of protective coatings
See more in Part 2. Compiled by: VTS technical team

Understanding Corrosion and How to Protect Against It

Rust and corrosion
Rust and corrosion, the unpleasant headache
Each year corroded machinery, buildings and equipment cost the industry billions of dollars. Corrosion is a costly problem. But by understanding its root causes, effective steps can be taken to prevent and combat it. There are several types of corrosion costs that plant workers must consider:
  • Direct loss or damage of metal structures due to corrosion. An example is a hot water tank that has corroded and must be scrapped.
  • Maintenance costs attributed to corrosion. Any metal surface that must be painted every few years to control corrosion falls into this area.
  • Indirect losses resulting from corrosion. These losses may result from leakage and fires. Explosions attributed to leakage, power failures, facility shutdown and labor losses are also indirectly the result of corrosion.
The first step toward controlling these costs requires understanding what corrosion is, and what causes it.

What is rust?

When iron or steel corrodes, the result is iron oxide, or what we call rust. Steel is mostly composed of iron ore. In its natural state, iron ore looks much like rust: dark red and finely grained, with a tendency to hold moisture. Iron ore is a stable substance until it is converted into iron or steel, naturally weaker elements. When steel is exposed to moisture and oxygen, it immediately starts regressing to its natural state. Although protective measures have been taken, a large part of the steel made in this century has already rust back to an oxide, its natural state. Three elements are required for corrosion to exist: a protected metal, a corroded metal, and a current-conducting medium between the two. When two dissimilar metals are brought into contact, one will become the protected metal, and the other will become the corroded metal. Plant operators may recognize environmental situations that are conducive to corrosion.

For example:

  • If galvanized fittings are used on steel pipe, the galvanized (zinc) fitting will become corroded, while the steel remains protected.
  • Steel or other metals under stress will become corroded, while the unstressed steel is protected from corrosion. This is the reason you see rust pitting on steel.
  • Freshly cut steel will corrode more rapidly. Threads cut on pipe will always rust first.
Even if a piece of steel is not in contact with another metal, neither under stress nor freshly cut, it will rust when exposed to the weather. This is because steel is not entirely uniform in composition – slight variations in density and composition will occur within a single piece of steel, which results in corrosion. The third ingredient needed for steel to corrode is an electrolyte. This is normally a liquid or water-containing substance that conducts the corrosion’s current from the protected metal to the corroded metal. The most common current-carrying substance is water. Rain, dew, humidity in the air, etc., all serve as efficient electric conductors. Steel corrodes very slowly in desert climates where humidity is low and rainfall rare. In areas of high humidity and frequent rain, protecting steel is critical. Plant operators will recognize some of the following environments that offer electric currents to speed the corrosion process:
  • Adding salt to water greatly enhances its current-carrying ability. Thus, steel exposed to seawater or salt spray will corrode more rapidly than steel in fresh water. Atmospheric corrosion is greater in areas near the oceans, due to the effect of salt air. Concentrated brine solutions, such as those used in the food-processing industry, cause severe corrosion.
  • Industrial smoke and fumes contain acids, alkalies and other chemicals, which serve as current conductors. Consequently, atmospheric corrosion in industrial areas is more severe than in rural areas.
  • Soil, clay and earth materials are also good conductors of electricity. Pipelines and other steel buried in the ground will be prone to corrosion unless protected. Just as soil varies considerably in composition, it also varies in its electric conductivity: some soils cause more severe corrosion than others.

Corrosion control

To make the use of steel and other metals practical in construction and manufacturing, some corrosion-protection practices must be employed. Otherwise, the life of steel and other metals will be limited, reducing efficiency and escalating the cost of maintenance. There are several effective ways to stop corrosion:
  1. Impressed current. By using suitable current-generating equipment and controls, it is possible to reproduce a current equal in strength to the corroding current, but flowing in the opposite direction. This type of protection is generally limited to pipelines, buried tanks, etc., and requires careful engineering and layout. Used improperly, an impressed current can promote corrosion.
  2. Sacrificial metals. Steel can be protected by adjacent placement to a dissimilar metal. For example, if zinc or magnesium is placed in direct contact with steel, it protects the steel from corrosion. Here, zinc and magnesium serve as sacrificial metals that not only protect the area of immediate contact, but also protect beyond the metal in each direction. Protection from rust by sacrificial metals is commonly used in several forms:
  • Zinc or magnesium blocks are often used to protect ship hulls, water tank interiors and other submerged surfaces.
  • Complete covering of the steel with the sacrificial metal is often done. Galvanized steel, for example, is steel covered with zinc. The zinc is sacrificial and will protect the base steel.
  • Zinc-rich coatings may be applied to a steel surface to provide cathodic protection. Zinc-rich coatings consist of 85% to 95% zinc metal in a suitable binder. The zinc particles, deposited by painting, protect the steel.
  1. Primers. Primers and finished coatings protect metal surfaces by providing a barrier between the steel and the corroding elements. They also prevent moisture from reaching the surface of the steel. A coating film protects underlying metal substrates in three ways:
  • Coatings can slow the rate of diffusion of water and oxygen from the environment to the metal surface. This slows the corrosion process.
  • The paint film can slow the rate of diffusion of corrosion products from the metal surface through the paint film. This also slows the corrosion process.
  • The anti-corrosive pigments contained in quality primers change the surface properties of the base metal. The metal develops a high electrical resistance as a result. Different pigments accomplish this reaction in different ways. Primers absorb and tie up moisture so that it does not react with the steel.
Painting solution works because it slows down corrosion by reducing the rate of current flow in the electrochemical corrosion process. HOWEVER, it is just a short-term remedy. After years of research and development, Nitto Denko from Japan just promoted a comprehensive solution to corrosion called Oxidation Polymerized Outdoor Anti-corrosion Tape NITOHULLMAC XG Series.

The product has 4 components:

  1. Primer Nitohullmac XG-PN: a synthetic fluid and a paste of non-solvent type primer that consists of rust preventatives, inert inorganic fillers and coloring agents etc. It has good waterproofing performance, inhibit rust advance by permeating rust layer because it is oil type.
  2. Outdoor anti-corrosion tape:made of plastic base non-woven fabric implemented with a compound which has a specially compounded drying oil as its main ingredient, form anti-corrosion layer, good weatherbility, can shut out water and air that will lead to corrosion of metal surface of cause of good adhesive tape compound and primer
  3. Nitohullmac XG Filler material Nitohullmac XG-M: a clay-like filler material added inert inorganic fillers and thickener, can be used as gap filler materials for irregular shaped parts like flange or valve; and
  4. Top coat Nitohullmac XG-T: a water based top coating material to improve outside appearance, durability and waterproofing performance for XG tape.
Click here for more details. Corrosion is now your terrible headache? Contact us +84981581661 for site survey and all-round solution.

  • Add/showroom: BT7-16, KĐT Văn Khê, Hà Đông, Hà Nội
    Inquiry: 038.224.1661
    Product consultation: 0789.000.134
    Email: vts@vinats.com

© 2016 Vinats. All rights reserved | powered by Jupiter Media

Chính sách thanh toán - Chính sách khiếu nại - Chính sách vận chuyển - Chính sách đổi trả và hoàn tiền - Chính sách bảo hành - Chính sách bảo mật thông tin

CÔNG TY TNHH VINA TRADE SYNERGY
GPKD số 0107475020 do Sở KH và ĐT TP Hà Nội cấp ngày 16/02/2016
Địa Chỉ: Thôn Yên Khê, X. Yên Thường, H. Gia Lâm, Tp. Hà Nội